Effect of Powder-Feeding Modes During Plasma Spray on the Properties of Tungsten Carbide Composite Coatings

摘要

A WC-reinforced composite coating was fabricated on the surface of 45 steel samples by plasma, cladding process with WC powder added to the molten pool synchronously or in the tail of the molten pool. The microstructure, phase composition, and element distribution in the coating were analyzed. The results show that the undissolved WC particles and crystallized carbide ( WC, (WC)-C-2) were distributed uniformly in the sub-eutectic matrix in both cases. Fewer of the WC particles are dissolved in the matrix when they are injected into the tail of the molten pool. There are fewer needle-like tungsten carbide formations seen in the composite coating fabricated by back-feeding process than in that formed by synchronous feeding. The former results in a finer microstructure and a higher concentration gradient of elements near the interface between the WC particles and the coating matrix.