Corrosion characteristic comparisons of ZrO2-, TiO2-coated and uncoated 316 stainless steel samples in supercritical water oxidation of municipal sludge

摘要

Supercritical water oxidation (SCWO) can efficiently and harmlessly dispose municipal sludge (MS), but typically faces severe reactor corrosion problems. In this work, 316 stainless steel (316SS) sample surface was processed by atmospheric plasma spraying to form a protective ZrO2 or TiO2 coating. The 316SS, ZrO2/316SS and TiO2/316SS samples were exposed to a typical MS SCWO environment (at 450 degrees C, 24 MPa and 1.2 of oxidation coefficient) for 20h-150 h. The results show that prolonging exposure time increased corrosion and surface coating could inhibit 316SS corrosion. ZrO2/316SS showed the best corrosion resistance among 316SS, ZrO2/316SS and TiO2/316SS, and its maximum corrosion rate was 0.0097 mg.cm(-2).h(-1). The oxide film of ZrO2/316SS after 150 h of corrosion exposure consisted of ZrO2, FeO, Fe2O3, NiO and Cr2O3, and its inner layer was rich in Cr2O3. The ZrO2 coating was much more stable than the TiO2 coating, and can be considered as the coating of the 316SS structure material for a MS SCWO reactor. (C) 2019 Elsevier B.V. All rights reserved.