机译:碳酸酯和碳酸氢盐离子在劣化混凝土的模拟孔隙溶液中发挥了预防的HRB400钢筋
为了评估HRB400 Rebars在混凝土老化过程中的腐蚀行为,提出了相应的模拟混凝土孔解决方案。 讨论了使用电化学测量和XPS分析,讨论了Depassivation条件,预防膜的性质和剥离腐蚀速率。 研究了碳酸盐和碳酸氢盐离子,pH和氯对预防HRB400 Rebars腐蚀行为的影响。 结果表明,在Dupassivation之前和之后,碳酸酯和碳酸氢盐离子对被动式HRB400钢筋的影响:在Depassivation,碳酸酯和碳酸氢盐离子之前对无源膜的稳定性有害,但在Dupassivation之后有益。 p> 部分> 摘要>
Corrosion and Protection Division Shenyang National Laboratory for Materials ScienceInstitute of Metal Research Chinese Academy of SciencesWencui Road 62 Shenyang 110016 P. R. China;
Corrosion and Protection Division Shenyang National Laboratory for Materials ScienceInstitute of Metal Research Chinese Academy of SciencesWencui Road 62 Shenyang 110016 P. R. China;
Corrosion and Protection Division Shenyang National Laboratory for Materials ScienceInstitute of Metal Research Chinese Academy of SciencesWencui Road 62 Shenyang 110016 P. R. China;
Corrosion and Protection Division Shenyang National Laboratory for Materials ScienceInstitute of Metal Research Chinese Academy of SciencesWencui Road 62 Shenyang 110016 P. R. China;
carbonate and bicarbonate ions; concrete; depassivation; pre‐passive HRB400 steel; XPS;
机译:碳酸酯和碳酸氢盐离子在劣化混凝土的模拟孔隙溶液中发挥了预防的HRB400钢筋
机译:碳酸氢根和碳酸根离子对模拟混凝土孔隙溶液中碳钢的抑制作用
机译:在不同碱度的模拟混凝土孔隙溶液中,生锈的钢筋的表面改性和增强的钝化/防腐性能
机译:不同模拟混凝土孔隙溶液环境下钼酸钠对钢筋钝化膜影响的研究
机译:钢铁在模拟混凝土孔隙溶液中的钝化和钝化过程的电化学和微观研究。
机译:新型耐腐蚀钢筋在模拟混凝土孔隙溶液中的钝化膜生长机理:纳米结构和电化学研究
机译:不同碱度模拟混凝土孔隙溶液中生锈钢筋的表面改造,具有不同碱度的模拟混凝土孔溶液中的钝化/防腐性能
机译:腐蚀抑制剂和环氧涂层增强钢在模拟混凝土孔隙水溶液中的防腐性能