Significantly enhanced mechanical properties of ZrAlCo bulk amorphous alloy by microalloying with Ta

摘要

AbstractThe alloy composition of Zr54Al17Co29with high glass forming ability (GFA) in the Zr-Al-Co system was predicted by using the multiple binary eutectic clusters from the phase diagram. Then the microalloying effects of Ta on the microstructure, thermal properties, mechanical properties, and corrosion resistance of (Zr54Al17Co29)100-xTax(x?=?0, 1, 1.5, 2, 2.5, 3) bulk amorphous alloy (BAA) were systematically investigated. The alloy composition with 1?at.% Ta alloy can be cast into BAA rods with diameters of 4?mm. The (Zr54Al17Co29)99Ta1exhibited high yield stress of 2553?MPa, high fracture strength of 3170?MPa, plastic strain of 8.6%, and low Young's modulus of 111?GPa with better corrosion resistance in comparison with the ZrCuNiAl BAA, ZrCuAlAg BAA, and 316L stainless steel in the Hank's Balanced Salt solution. The Ni-, Cu-, Be-free (Zr54Al17Co29)99Ta1bulk amorphous alloys with a critical diameter up to 4?mm, excellent mechanical properties, superior corrosion resistance are believed to be useful in orthopedic applications.Highlights?Zr54Al17Co29with high GFA was predicted by using the multiple binary eutectic clusters from the phase diagram.?The compressive strength and plastic strain of the ZrAlCoTa1BAA are 3.17?GPa and 8.6%.?The ZrAlCoTa1BAA shows superior corrosion resistance in HBSS to that of SUS316L steel.]]>