CuInSe2 Thin-Film Solar Cells with 7.72?% Efficiency Prepared via Direct Coating of a Metal Salts/Alcohol-Based Precursor Solution

摘要

A simple direct solution coating process for forming CuInSe2 (CIS) thin films was described, employing a low-cost and environmentally friendly precursor solution. The precursor solution was prepared by mixing metal acetates, ethanol, and ethanolamine. The facile formation of a precursor solution without the need to prefabricate nanoparticles enables a rapid and easy processing, and the high stability of the solution in air further ensures the precursor preparation and the film deposition in ambient conditions without a glove box. The thin film solar cell fabricated with the absorber film prepared by this route showed an initial conversion efficiency of as high as 7.72?%.