The linear tearing properties of biaxially oriented PA6/MXD6 blending films

摘要

The main purpose of this work was to investigate the linear tearing properties of PA6/MXD6 films prepared by simultaneous biaxial stretching. The compatibility between PA6 and MXD6 and the thermal properties of the PA6/MXD6 composites were also investigated. The results showed that the tearing deviation of the blending films decreased from 100 to 3.8% when the MXD6 blend ratio increased from 0 to 25%, but the deviation increased when the MXD6 blend ratio continue to increase. It means that the PA6/MXD6 films with addition of 25 wt% MXD6 exhibited the best linear tearing properties. The differential scanning calorimetry results revealed that the addition of MXD6 reduced the melting temperature from 227.5 to 224.8 degrees C and crystallization temperature of PA6 from 179.3 to 175 degrees C due to the benzene ring structure of MXD6. The dynamic mechanical analysis results indicated that MXD6 exhibits favorable compatibility with PA6. In addition, it was found that the barrier properties of the biaxially oriented PA6/MXD6 films were extremely improved with the increase of MXD6 content.