Preparation, characterization and properties of starch-based adhesive for wood-based panels

摘要

A new biodegradable, renewable, and environmentally friendly starch-based adhesive for wood-based panels was synthesized. The synthesis was conducted by grafting polymerization of vinyl acetate (VAC) monomer onto corn starch and crosslinking polymerization with N-methylol acrylamide (NMA). Compared with the traditional starch-based wood adhesive, the water resistance of starch-based adhesive with NMA (SWA-N) was greatly improved to more than 1 MPa; this exceeds the Chinese standard by 40%. The results from various analyses, including particle size, contact angle, thermogravimetric analysis (TGA), Fourier-transform infrared (FTIR), confocal Raman microscopy (CRM) and C-13-CPMAS, indicated that such improved performance is due to increased crosslinking density and formation of complex network structure. Such complex network structure was found to inhibit excessive expansion of the adhesive during high temperature pressing and water absorption. As a result, the internal structure of the adhesive remained intact when subjected to hot pressing and placed in wet conditions. (C) 2019 Elsevier B.V. All rights reserved.