Flow accelerated corrosion and its control measures for the secondary circuit pipelines in Indian nuclear power plants

摘要

A plain carbon steel feeder pipeline in the secondary circuit failed downstream of a flow measurement device (orifice meter) during operation at nuclear power plant. A detailed failure analysis done on the failed pipeline is described in this paper. The results established the fine surface pattern of 'Horseshoe pits' at the affected regions. X-ray diffraction analysis on the samples far from the failed regions showed presence of magnetite but on the sample from the failed region showed peaks due to base metal only, indicating dissolution of the oxide. Thickness profiling of the pipeline indicated reduction of thickness from the design 7.62 mm to a minimum of 0.4-1.4 mm at the location of the failure. These observations are characteristic of single phase flow accelerated corrosion. This paper details the extent of flow accelerated corrosion in various Indian power plants and the remedial measures for replacement and possible design and water chemistry changes to combat it.