Microstructures and high temperature oxidation resistance of alloys from Nb-Cr-Si system

摘要

Oxidation behavior of Nb-30Si-(10,20)Cr alloys have been evaluated in air from 700 to 1400 °C by heating for 24 h and furnace cooling them. The lower weight gain per unit area has been observed for 20Cr alloy at 1200, 1300, and 1400 °C. Pesting has been observed at lower temperatures (700, 800, 900 °C). Analysis indicates that the powder formation at 900, 100, 1100 °C may be associated with β form of Nb_2O_5 (base centered monoclinic form). However the m-monoclinic form of Nb_2O_5 evolves at temperatures above 900 °C while o-orthorhombic Nb _2O_5 forms at below this temperature. The phases in the alloys have been calculated using the Pandat~(TM) software program at different temperatures using calculated Nb-Cr-Si phase diagrams.