Photoelectrochemical water splitting on chromium-doped titanium dioxide nanotube photoanodes prepared by single-step anodizing

摘要

Cr-doped TiO2 nanotubes (Cr-TiO2NTs) with different amounts of chromium were obtained directly by the electrochemical anodic oxidation of titanium foils in a single-step process using potassium chromate as the chromium source. The effects of chromium amount in anodizing solution on the morphologies, structure, photoabsorption and photoelectrochemical water splitting of the TiO2 nanotube array film were investigated. Diffuse reflectance spectra showed an increase in the visible absorption relative to undoped TiO2NTs. The photoelectrochemical performance was examined under visible irradiation in 1 M NaOH electrolyte. Photo-electrochemical characterization shows that chromium doping efficiently enhances the photo-catalytic water splitting performance of Cr-doped TiO2 nanotube samples. The sample (Cr-TiO2NTs-1) exhibited better photo-catalytic activity than the undoped TiO2NTs and Cr-TiO2NTs fabricated using other chromium concentrations. This can be attributed to the effective separation of photogenerated electron-hole upon the substitutional introduction of appropriate Cr amount in to the TiO2 nanotube structure. (C) 2015 Elsevier B.V. All rights reserved.