Controlling micro- and nanofibrillar morphology of polymer blends in low-speed melt spinning process. Part I. Profiles of PLA/PVA-filament parameters along the spinline

机译:在低速熔体纺丝过程中控制聚合物共混物的微纤维和纳米原纤维形态。第一部分。沿着纺丝线的PLA / PVA丝参数分布

获取原文
获取原文并翻译 | 示例
       

摘要

The profiles of PLA/PVA filament parameters (e.g., temperature, velocity, tensile stress, and apparent elongational viscosity) along the spinline in the low-speed melt spinning process under various spinning conditions were investigated. Owing to the combination of the filament velocity and filament temperature measurements using laser doppler velocimetry (LDV) and infrared thermography, respectively, the fiber formation zone was determined. The length of the fiber formation zone obtained from filament velocity profiles LSv is always shorter than that obtained from the filament temperature profiles LST ( LSv
机译:研究了在各种纺丝条件下低速熔体纺丝过程中沿纺丝线的PLA / PVA长丝参数分布(例如温度,速度,拉伸应力和表观伸长粘度)。由于分别使用激光多普勒测速仪(LDV)和红外热像仪对细丝速度和细丝温度进行了测量,因此确定了纤维形成区域。从细丝速度曲线LSv获得的纤维形成区的长度总是比从细丝温度曲线LST获得的纤维形成区的长度(LSv <LST)短。显然,由于长丝沿纺丝线的轴向热传导效应以及穿过横截面粗丝的径向温度分布不均匀,这种低速纺丝时会发生这种意外现象。另一个非凡的发现与Nusselt数有关,在低速熔体纺丝过程中,沿着纺丝线的Nusselt数几乎恒定。因此,将大大简化灯丝温度曲线的数学模拟。 (c)2016 Wiley Periodicals,Inc. J. Appl。 Polym。科学2016,133,44258。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱:kefu@zhangqiaokeyan.com

京公网安备:11010802029741号 ICP备案号:京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有
  • 客服微信

  • 服务号