Current induced surface diffusion on a single-crystalline silver nanowire

摘要

Scanning tunnelling microscopy was used to study the morphological changes of the surface of a single-crystalline silver nanowire caused by a lateral electron current. At current densities of about 1.5×10 ~7 A cm ~(-2), surface atoms are extracted from step edges, resulting in the motion of surface steps, islands and holes with a thickness or depth of one monolayer. Upon current reversal the direction of the material transport can be altered. The findings are interpreted in terms of the wind force.