Influence of slag chemistry on the hydration of alkali-activated blast-furnace slag - Part II: Effect of A1_2O_3 N^M. Ben HahaEmpa, Swiss Federal Laboratories for Materials Science and Technology, Laboratory for Concrete and Construction Chemistry, Ueberiandstrasse 129, 8600 Diibendorf, Switzerland

摘要

The hydration and microstructural evolution of three alkali activated slags (AAS) with A1_2O_3 contents between 7 and 17%wt.% have been investigated. The slags were hydrated in the presence of two different alkaline activators, NaOH and Na_2SiO_3-5H_2O. The formation of C(-A)-S-H and hydrotalcite was observed in all samples by X-ray diffraction, thermal analysis and scanning electron microscopy. Higher A1_2O_3 content of the slag decreased the Mg/Al ratio of hydrotalcite, increased the Al incorporation in the C( - A)-S-H and led to the formation of stratlingite. Increasing A1_2O_3 content of the slag slowed down the early hydration and a lower compressive strength during the first days was observed. At 28 days and longer, no significant effects of slag A1_2O_3 content on the degree of hydration, the volume of the hydrates, the coarse porosity or on the compressive strengths were observed.