Synthesis and Properties of Poly(1,8-Diaminonaphthalene) using Tetravalent Cerium as Oxidant

摘要

The poly(1,8-diaminonaphthalene) (P18DAN) was readily synthesized by chemical oxidative polymerization. The structure of Ce~(3+)-P18DAN was characterized by the spectra of FT-IR, Raman, UV-VIS and WXRD. Red-shifted change for the quinoid and benzenoid structure stretching vibration are observed in ER and Raman spectra after doping Ce~(5+) ions and a new UV absorption peak presents at 610 nm. The results show that the interaction had occurred between Ce~(3+) ions and amino or imine groups on P18DAN backbone. A more keen-edged diffractive peak is exhibited at 29 = 24.3° for Ce~(3+)-P18DAN in WXRD, while the peak at 16.9° ascribed to the periodicity parallel chains disappears. Comparing to H~+-P18DAN, the excitation and emission peaks centered at 388 nm and 512 nm, respectively, have a red-shifted for 51 nm and 107 nm. Additionally, the conductivities of P18DAN are increased from 2,37 x 10~(-6) to 5.70 x 10~(-4) S cm~(-1) after doping Ce~(3+) ions, suggesting that the degree of electrons derealization are improved by complexing with Ce~(3+) ions.