1050一H24アルミニウム板の対向液圧付加による深絞り限界の低下とその対策

摘要

Influence of hydraulic counterpressure on the deep drawability of an aluminum work hardening sheet, and the forming method for improving deep drawing limit are examined. When a 1050-H24 aluminum sheet is formed by hydraulic counterpressure deep drawing, the limiting drawing ratio decreases compared with one formed by the conventional deep drawing. This is caused by inverse bulging deformation generated between a punch and a die due to hydraulic counterpressure. The radial strain caused by the inverse bulging deformation concentrates on the punch profile radius, which causes the local decrease of sheet thickness. For this reason, it is impossible to encourage material inflow into the die from a flange part. For relieving locally concentrated strain caused by inverse bulging deformation, material inflow into the die from the flange part is necessary. For this purpose, a method to push the flange edge by radial pressure drawing is effective. In addition, for suppressing the inverse bulging deformation generated under high liquid pressure, a method to reduce a blank holder profile radius and restraining by the metallic mold is effective.延性の乏しい加工硬化した工業用純アルミニウム板（1050－H24）の円筒絞りにおける対向液圧の効果を調べ，次のことを明らかにした。 加工硬化した工業用純アルミニウム板を従来の対向液圧法で探絞り加工すると慣用金型法よりも限界絞り比が低下する。 限界絞り比が低下する理由は，対向液圧によって発生する逆張出変形による半径方向引張ひずみが，パンチ肩部に集中して局部的な板厚減少を起こし，フランジ部からの材料流入を促すことができないためである。 逆張出変形によって生じるひずみの局部集中を抑制するには，フランジ部からダイ内への材料流入が必要であり，その方法として周液圧探絞り法によるフランジ押込み効果が有効である。フランジ押込み効果は，液圧が高いほど効果があるが，逆張出変形による板厚減少が大きくなるため適正値が存在する。 高い液圧下で発生する逆張出変形を抑制するにほ，しわ抑え板とパンチとの隙間の減少，しわ抑え板肩部半径の減少など，金型による強制的抑制法が有効となる。