The Influence of Humidity on Fatigue Crack Propagation Properties in Spherical Graphite Cast Iron

摘要

The fatigue crack propagation test was carried out in order to clarify the effect of humidity on the characteristics of fatigue crack propagation in spherical graphite cast iron. Spherical graphite cast iron (FCD450) was used as a specimen. Then, two kinds of heat treatments were conducted to the material. One was an austemper treatment (ADI), the other was a quenching and tempering treatment (QT). Moreover, as cast material was added, and with these three materials fatigue crack propagation test was carried out. The experiment conformed to ASTM. Stress ratio R was 0.1, and specimen used was 1CT type, 12.5mm thick. The test was carried out at room temperature and under three or four kinds of humidity, 0, 20, 40, 60, 80 percent. The relationship between the characteristics of fatigue crack propagation and the crack closure which produced on fracture surface, was investigated. The obtained results were as follows. In the low DELTA K region, since the oxide inducement crack closure is generated, the propagation speed lowered, and DELTA Kth increased. In high DELTA K region of QT and ADI, the fatigue crack propagation speed was accelerated by the effect of humidity. DELTA Kth of As-cast and QT were increased with the rise in humidity. DELTA Kth of the ADI was highest in the humidity 40 percent atmosphere. However, it couldn't be clarified that the factor of decreasing DELTA Kth over the 40 percent.