Effect of the polycarbosilane structure on its final ceramic yield

摘要

The ceramic yield of a new polycarbosilane is discussed based on its structure, including vinyl functionality, branched structure, as well as polymer molecular weight. The cross-linking behavior of this polymer is studied up to 400 deg C. According to the cross-linking mechanism, the optimized heat-treatment conditions can be obtained for a high ceramic yield. The product pyrolysized at 1400 deg C has a composition close to 1.1:1 Si:C with a ceramic yield of about 70 percent.