Influence of PbCl2 content in PbI2 solution of DMF on the absorption, crystal phase, morphology of lead halide thin films and photovoltaic performance in planar perovskite solar cells

摘要

In this paper, the influence of PbCl2 content in PbI2 solution of DMF on the absorption, crystal phase and morphology of lead halide thin films was systematically investigated and the photovoltaic performance of the corresponding planar perovskite solar cells was evaluated. The result revealed that the various thickness lead halide thin film with the small sheet-like, porous morphology and low crystallinity can be produced by adding PbCl2 powder into PbI2 solution of DMF as a precursor solution. The planar perovskite solar cell based on the 300-nm-thick CH3NH3PbI3-xClx thin film by the precursor solution with the mixture of 0.80 M PbI2 and 0.20 M PbCl2 exhibited the optimum photoelectric conversion efficiency of 10.12% along with an open-circuit voltage of 0.93 V, a short-circuit photocurrent density of 15.70 mA cm(-2) and a fill factor of 0.69. (C) 2015 Elsevier Inc. All rights reserved.