Preparation and nonlinear optical properties of Au nanoparticles doped TiO2 thin films

摘要

Nano-sizcd noble metal nanoparticles doped dielectric composite films with large third-order nonlinear susceptibility due to the confinement and the enhancement of local field were considered to be applied for optical information processing devices, such as optical switch or all optical logical gates. In this paper, sol-gel titania thin films doped with gold nanoparticles (AuNPs, ~ 10 nm in average size) were prepared. AuNPs were firstly synthesized from HAuCl4 in aqueous solution at ~60 °C, using trisodium citrate as the reducing agent, polyvinylpyrrolidone as the stable agent; then the particle size and optical absorption spectra of the AuNPs in aqueous solutions were characterized by transmitting electron microscopy and UV-Vis-NIR spectrometry. Sol-gel 2AuNPs-100TiO2 (in %mol) thin films (5 layers, ~ 1 μm in thickness) were deposited on silica glass slides by multilayer dip-coating. After heat-treated at 300-1,000 °C in air, the AuNPs-TiO2 thin films were investigated by X-ray diffraction, scanning electron microscopy and atomic force microscopy. The nonlinear optical properties of the AuNPs-TiO2 thin films were measured with the Z-scan technique, using a femtosecond laser (200 fs) at the wavelength of 800 nm. The third-order nonlinear refractive index and nonlinear absorption coefficient of 2AuNPs-100TiO2 films were at the order of 10~(-12) cm~2/W, and the order of 10~(-6) cm/W, respectively, and the third-order optical nonlinear susceptibility χ~(3) was ~6.88 × 10~（-10） esu.