Fabrication and physical properties of lanthanide oxide glass wasteform for the immobilization of lanthanide oxide wastes generated from pyrochemical process

摘要

The pyrochemical process, which uses a dry method to recycle used nuclear fuel generates waste LiCl–KCl salt containing radioactive lanthanide elements. To reuse LiCl–KCl salt, the lanthanide elements are separated through a precipitation method promoted by oxygen sparging and the separated fission product of lanthanide oxide should be fabricated into durable wasteforms sustainable for several 1,000 years to store in a final geological repository. Herein, we report the fabrication of a borosilicate glass based wasteform with a glass matrix of SiO_2–Al_2O_3–B_2O_3 having a high waste loading of 50 wt% lanthanide oxide. Th physical properties of four kinds of wasteforms having a different lanthanide oxide waste composition were evaluated. To investigate the long-term physical stability of each sample having 50 wt% lanthanide oxide waste loading, time–temperature–transformation (TTT) test was conducted at 500 and 700 ℃ for 60 and 180 h, and the physical properties were evaluated after each TTT test.