Unique microstructure analysis of ethylene-propylene copolymer synthesized using catalytic system based on α-diimine nickel complexes: a comparative study by ~(13)C NMR technique

摘要

The microstructure of rubber-like ethylenepropylene copolymer (MN4) produced by a mixed nickelbased system (MN) containing catalysts of dibromo[N,N′-bis(2,6-diisopropylphenyl)-2,3-butanediimine]nickel(II) n1 and dibromo[N,N′-(phenanthrene-9,10-diylidene)bis(2,6-diisopropylaniline)]nickel(II) n2 was determined by 13C NMR technique. Sequences distribution of ethylene (E), propylene (P), EP, inverted propylene and uninterrupted methylene and also methylene number-average sequence lengths for the copolymer (MN4) were estimated. The results obtained from the MN4 EP copolymer were compared with reported copolymers which had been synthesized using constrained geometry catalyst (CGC) and vanadium-based Ziegler-Natta catalyst. The results demonstrated that the MN4 EP copolymer had fewer alternating comonomer sequences than ethylene-propylene elastomers obtained by CGC and vanadium-based (V) catalysts. A large number of the inversion structures (66 %) and high mole percent of sequences containing a long branch (3.2 mol%) were also observed in unique microstructure of the copolymer (MN4).