Effect of obturating systems, dowel materials, and adhesive luting techniques on the resistance to fracture of endodontically treated teeth.

摘要

PURPOSE: The aim of this study was to assess the role of obturating systems, dowel materials, and adhesive techniques on the resistance to fracture of endodontically treated teeth. MATERIAL AND METHODS: Eighty maxillary central incisors were selected and randomly divided into two groups according to the obturating system (n = 40); group I: gutta-percha and Roeko sealer; group II: RealSeal. Both groups were further subdivided into two subgroups; subgroup A: using ceramic dowels (Cosmopost); subgroup B using fiber dowels (Easy Post). Each subgroup was assigned to two divisions according to the adhesive luting technique; division V (total-etch) Variolink II resin cement; division U (self-adhesive) RelyX Unicem. Composite core build-up was made using a core former. Each specimen was loaded 2 mm from its incisal edge on the palatal side at a 135 degrees angle with the long axis of the tooth using a universal testing machine with a load cell of 5 KN at a crosshead speed of 0.5 mm/min until fracture. Failure loads were recorded in N. Scanning electron microscopic examination at the dentin/resin interface (1000x) was performed. Three-way ANOVA was used to test the effect of obturating system, dowel material, adhesive technique, and their interactions (obturating system * dowel material, obturating system * adhesive, dowel material * adhesive, obturating system * dowel material * adhesive). Duncan's test was used for pairwise comparison. The significance level was set at p