Crack Initiation from Corrosion Pit in Three Aluminum Alloys Under Ambient and Saltwater Environments

摘要

Corrosion-pit-to-crack transition behaviors of three aluminum alloys using two pit configurations were investigated under ambient and saltwater environments. Fatigue stress ranges for crack initiation from a through-pit were less than that from a corner-pit in both environments in all three materials, while stress intensity factor ranges showed the opposite trend. Further, stress ranges or stress intensity factor ranges for crack initiation were less in saltwater than that in ambient environment for both pit configurations. Fatigue damage mechanisms in a test environment were similar for both pit configurations in all three materials. An empirical relationship is proposed to estimate pit-to-crack transition fatigue cycles.