Indole Alkaloids of Alstonia angustifolia var. latifolia as Green Inhibitor for Mild Steel Corrosion in 1 M HCl Media

摘要

The inhibition effect of mild steel (MS) corrosion in 1 M HCl was studied by the addition of indole alkaloids (crude) isolated from Alstonia angustifolia var. latifolia (A. latifolia) leaves at 303 K. Potentiodynamic polarization, impedance spectroscopy, scanning electron microscopy (SEM), and Fourier transform infrared (FTIR) analyses were used for this study. Results show that the isolated alkaloid extract of A. latifolia is a good inhibitor and exhibited maximum inhibition efficiency (above 80%) at concentrations between 3 and 5 mg/L. Polarization measurements indicated that the inhibitor does not alter the mechanism of either anodic or cathodic reactions and acted as mixed-type inhibitor. The inhibition efficiencies of both electrochemical techniques are found to be in good agreement and adsorption of inhibitor follows Langmuir isotherm. Adsorption of inhibitor over metal surface was well supported by the SEM studies, while FTIR studies evidenced the presence of indole alkaloids as green inhibitor that reduces the rate of corrosion.