Dinuclear platinum complexes containing aryl-isoquinoline and oxadiazole-thiol with an efficiency of over 8.8%: in-depth investigation of the relationship between their molecular structure and near-infrared electroluminescent properties in PLEDs

摘要

Two novel dinuclear platinum complexes of (2niq)(2)Pt-2(mu-C8PhOXT)(2) and (piq)(2)Pt-2(mu-PhOXT)(2) were synthesized and characterized, where 2niq is 2-naphthyl-isoquinolinate, piq is 1-pheny-isoquinolinate, and mu-C8PhOXT and mu-PhOXT are anions of 5-(4-octylphenyl)-1,3,4-oxadiazole-2-thiol and 5-phenyl-1,3,4-oxadiazole-2-thiol, respectively. The Pt-Pt bond was confirmed by the (piq)(2)Pt-2(mu-PhOXT)(2) single crystal. A high-efficiency NIR electroluminescence peak at about 704 nm was observed for this (2niq)(2)Pt-2(mu-C8PhOXT)(2) in the solution-processed PLEDs with a notable external quantum efficiency (EQE) of 8.86% and an irradiate of 986 mW cm(-2) at 9 wt% dopant concentration. Moreover, the efficiency roll-off was efficiently restrained, with an EQE of 5.22% at a current density of 100 mA cm(-2) and 8.47% at 12 wt% dopant concentration.