Discontinuous nickel filaments of diameter 0.4 μm and having a carbon core of diameter 0.1 μm were fabricated by electroplating nickel on discontinuous carbon filaments. They exhibited a grain size of 0.016 μm and electrical resistivity of about 5×10~(-6) Ω cm. In an amount as low as 7 vol.% in a polymer (polyether sulfone) matrix, they resulted in a composite exhibiting electromagnetic interference shielding effectiveness of 87 dB and reflection coefficient 0.95 at 1-2 GHz, tensile strength 52 MPa, tensile ductility 1.0%, and density 1.87 g/cm~(3).