Effect of Rare Earth Element Addition on the Microstructure of Sn-Ag-Cu Solder Joint

摘要

The effects of minimal rare earth (RE) element additions on the microstructure of Sn-Ag-Cu solder joint,especially the intermetallic compounds (IMCs),were investigated.The range of RE content in Sn-Ag-Cu alloys varied from 0 wt.% to 0.25 wt.%.Experimental results showed that IMCs could be dramatically repressed with the appropriate addition of RE,resulting in a fine microstruc-ture.However,there existed an effective range for the RE addition.The best RE content was found to be 0.1 wt.% in the current study.In addition to the typical morphology of Ag_3Sn and Cu_6Sn_5 IMCs,other types of IMCs that have irregular morphology and uncertain constituents were also observed.The IMCs with large plate shape mainly contained Ag and Sn,but the content of Ag was much lower than that of Ag_3Sn.The cross sections of Cu_6Sn_5 IMCs whiskers showed various morphologies.Furthermore,some eutectic-like structures,including lamellar-,rod-,and needle-like phases,were observed.The morphology of eutectic-like structure was related to the RE content in solder alloys.When the content of RE is 0.1 wt.%,the needle-like phase was dominant,while the lamellar structure prevailed when the RE content was 0.05 wt.% or 0.25 wt.%.It is suggested that the morphology change of the eutectic-like structure directly affects the creep properties of the solder joint.