Effect of Heat Treatments on the Structural and Magnetic Properties of La-Co Substituted Strontium Ferrite Films

摘要

A sputter-deposited strontium ferrite film with perpendicular anisotropy has been developed. The film, composed of La0.33Sr0.67Co0.25Fe11.75O19, has been fabricated directly on quartz glass substrates by radio frequency magnetron sputtering with various heat treatments. The structural and magnetic property dependence of those films on heat treatments has also been studied. The optimized condition is the heat treatment of in situ heating at 400A degrees C and post-annealing at 850A degrees C-900A degrees C. When post-annealing temperature exceeds 900A degrees C, parasitic phases of gamma-Fe2O3 and LaFeO3 appear and gradually increase; meanwhile, the magneto plumbite phase gradually decreases. High c-axis perpendicularly oriented films with the coercivity (4148 Oe), remanence squareness ratio (0.89) and perpendicular magnetic anisotropy energy density (1.65 x 10(6) erg/cm(3)) are achieved, which is attributed to the single magneto plumbite phase with compact platelet grains and almost complete (0 0 l) texture of the c-axis normal to the film plane.