Multiple autoclave cycle effects on cyclic fatigue of nickel-titanium rotary files produced by new manufacturing methods.

摘要

INTRODUCTION: Novel nickel-titanium rotary files with proprietary manufacturing techniques have recently been marketed. The purpose of this study was to assess multiple autoclave cycle effects on cyclic fatigue of GT Series X files (Dentsply Tulsa Dental Specialties, Tulsa, OK) and Twisted Files (SybronEndo, Orange, CA) METHODS: A jig using a 5-mm radius curve with 90 degrees of maximum file flexure was used to induce cyclic fatigue failure. Files (n = 10) representing each experimental group (GT Series X 20/.04 and 20/.06; Twisted Files 25/.04 and 25/.06) were first tested to establish baseline mean cycles to failure (MCF). Experimental groups (n = 20) were then cycled to 25% of the established baseline MCF and then autoclaved. Additional autoclaving was accomplished at 50% and 75% of MCF followed by continual testing until failure. Control groups (n = 20) underwent the same procedures except autoclaving was not accomplished. RESULTS: The GT Series X (20/.04 and 20/.06) files showed no significant difference (p = 0.918/p = 0.096) in MCF for experimental versus control files. Twisted Files (25/.04) showed no significant difference (p = 0.432) in MCF between experimental and control groups. However, the Twisted Files (25/.06) experimental group showed a significantly lower (p = 0.0175) MCF compared with the controls. CONCLUSIONS: Under the conditions of this evaluation, autoclave sterilization significantly decreased cyclic fatigue resistance of one of the four file groups tested. Repeated autoclaving significantly reduced the MCF of 25/.06 Twisted Files; however, 25/.04 Twisted Files and both GT Series X files tested were not significantly affected by the same conditions.