Effect of temperature on post-cure polymerization of bulk-fill composites

摘要

Objectives: To investigate the 24 h post-cure polymerization and the effect of temperature on the post-cure polymerization of one conventional and three bulk-fill composite materials. Methods: A conventional composite GrandioSO (GR) and three bulk-fill composites: Tetric EvoCeram Bulk Fill (TECBF), Quixfil (QF) and X-tra fil (XF) were investigated. The samples were cured for 20 s with irradiance of 1090 mW/cm2. Composite samples were divided into two groups: the "room-temperature" group (RT, n = 5) and the "body-temperature" group (BT, n = 5) and they were stored in dark at 20°C and 37°C, respectively. Measurements of degree of conversion (DC) were made immediately after curing (0 h) and 24 h post-cure (24 h). To analyse the extent of post-cure DC increase, the DC values of 0 h-RT/24 h-RT and 0 h-BT/24 h-BT were compared. To analyse the difference in DC between RT and BT, the DC values of 0 h-RT/0 h-BT and 24 h-RT/24 h-BT were compared. Results: DC increase 24 h post-cure was significant for all composites and ranged between 6.3% and 8.2% in RT and between 12.5% and 15.7% in BT. All composites demonstrated a higher DC in 24 h-BT compared to 24 h-RT. The difference was statistically significant for GR, TECBF and QF. Conclusions: All composites demonstrated a significant post-cure effect after 24 h. Post-cure temperature increase from 20°C to 37°C yielded a higher post-cure DC increase. Clinical significance: Due to the temperature effect on the final DC, studies performed at composite samples at room temperature may record more inferior properties than these attained in the oral cavity.