CRYSTALLIZATION OF POLY(HYDROXYBUTYRATE-CO-HYDROXYVALERATE) IN WOOD FIBER-REINFORCED COMPOSITES

摘要

Wood fiber-reinforced composites were prepared from poly(hydroxybuty rate) (PHB) and poly(hydroxybutyrate-co-hydroxyvalerate) (PHB/HV) copolymers containing 9 and 24% valerate. The effects of fibers on crystallization-were investigated. Thermomechanical pulp, bleached Kraft fibers, and microcrystalline cellulose filler were used as the reinforcing phase. The crystallization of PHB/HV in composite materials was examined using Modulated Differential Scanning Calorimetry (MDSC) and hot-stage microscopy. Hot-stage microscopy showed that polymer crystallites are nucleated on the fiber surface and that the density of nuclei was greater in fiber-reinforced composites than in unfilled material. Dynamic crystallization experiments showed that bleached Kraft, thermomechanical pulp, and microcrystalline cellulose increased the crystallization rate of PHB and PHB/HV both from the glass and melt. However, ultimate crystallinity determined from the heat of crystallization was the same in unreinforced and reinforced materials. The kinetics of PHB/HV crystallization were examined using nonisothermal Avrami-type analysis. Unreinforced and Kraft-reinforced PHB were characterized and compared with unreinforced PHB/9%HV. The Avrami exponent of crystallization, related to nucleation mechanism and growth morphology, is 2.0 for unreinforced PHB, 2.8 for kraft-reinforced PHB, and 3.0 for unreinforced PHB/9%HV. (C) 1997 John Wiley & Sons, Inc. [References: 21]