Development of asymmetric BTDA-TDI/MDI (P84) copolyimide flat sheet and hollow fiber membranes for ultrafiltration: Morphology transition and membrane performance

摘要

In this paper, the effects of γ-butyrolactone (GBL) weight ratio (w_(Cbl)) and membrane thickness on the formation of asymmetric flat sheet membranes prepared with P84 (BTDA-TDI/MDI co-polyimide)/N-methyl-2-pyrrolidone (NMP)/GBL casting solutions are investigated. With the increase of membrane thickness, the transition of membrane morphology from sponge-like to finger-like structure occurs at critical structure-transition thickness L_c. L_c and the general sponge-like structure thickness (L_(gs)) increase with w_(Gbl)- For 20 wt.% P84/ NMP/GBL casting solution, the membrane morphology changes from finger-like to sponge-like structure at the critical weight ratio of GBL (w* = 0.69). The membrane morphology and performance of hollow fibers spun with various w_(GBL) are observed. Compared with the hollow fiber membranes made of 18 wt.% P84/ NMP/GBL dope solution with w_(Cbl)=0.75, the hollow fiber membranes spun with w_(GBl) = 0.25 present a higher permeation flux and a larger MWCO. As w_(Gbl) increases from 0.25 to 0.75, the membrane morphology transfers from finger-like to sponge-like structure. An increase in shear rate shifts the rejection curves towards left and lowers the MWCO of hollow fiber membranes. For hollow fiber membranes spun with w_(GBl) = 0.75, a relatively high permeation flux and a large MWCO are obtained by the wet spinning process.