Supersonic plasma sprayed MoSi2-ZrB2 antioxidation coating for SiC-C/C composites

摘要

A dense and crack free MoSi2-ZrB2 coating was prepared on the SiC coated carbon/carbon (C/C) composites using a supersonic plasma spraying technique. The coated composites were characterised using scanning electron microscopy and X-ray diffraction. The analysis shows that the as prepared MoSi2-ZrB2 coating, with a thickness of,100 mm, combines well with the inner SiC coating. After oxidation at 1200 degrees C for 72 h in air, the mass loss of MoSi2-ZrB2/SiC coated C/C is only 4.24 wt-%, which is significantly lower than that of MoSi2/SiC coated C/C (11.35 wt-%). The excellent oxidation protective ability of the MoSi2-ZrB2 coating is mainly attributed to ZrSiO4 produced by dispersive ZrO2 particles and SiO2 in the coating at high temperature.