Creep behaviour and long-term creep life extrapolation of alloy 617 for a very high temperature gas-cooled reactor

摘要

Creep behaviours for Alloy 617, such as creep properties, oxidation and creep fracture morphologies were investigated by a series of creep tests with different stress levels at 1223 K. Creep constants of A, n, m, and C were obtained at 1223 K for Alloy 617. To accurately predict the long-term creep life (or strength) for Alloy 617, a multi constant method with two C in the Larson-Miller (LM) parameter was newly proposed instead of the conventional one with a unique C. The conventional method did not thoroughly match with the creep rupture data, and revealed an overestimation for the prediction of the long-term creep strength. On the other hand, the multi constant method revealed a good agreement with the creep rupture data, and this method was more accurate than the conventional one. The multi constant analysis can be used to accurately predict the long-term creep rupture life of Alloy 617 above 105 h for 1173 K, 1223 K and 1273 K.