In situ resistivity and magnetoresistance studies of Co/Au(111) single layers and bilayers

摘要

We report here on resistance and magnetoresistance (MR) studies of ultrathin Co/Au(111) single sandwiches and bilayers with perpendicular magnetization. Resistance of the films was measured in situ in ultrahigh vacuum, during depositions and as a function of a perpendicular applied magnetic field. A large MR variation with the thickness of Au coverage was observed and compared to calculations. The coercive field of the Co films shows a drastic variation with the Au coverage thickness, which reflects the theoretical anisotropy variation. It was measured as a function of temperature. For the first time, the effect of interlayer interaction on the resistivity of a Co bilayer during the growth of Co top layer, is evidenced and compared to calculations. Finally, hysteresis loops of strongly antiferromagnetically coupled bilayers are investigated.