This paper illustrates the potential for separation of nm magnetic particles from viscous flows with a brief discussion of a novel magnetic method for breaking tight emulsions(U.S.Patent No.5,868,939)which was the forerunner of a new primary separator,the Magnetic Micro-Particle Separator,(MM-PS,patent pending).The remainder of the paper will focus on the MM-PS which was designed for high throughput isothermal and isobaric separation of nm iron catalyst particles from Fischer-Tropsch wax at 260deg C.Using magnetic fields up to 2,000 gauss,F-T wax with 0.3- 0.5 wt% solids was produced from 25 wt% solids F-T slurries at product rates up to 230 kg/min/m~2.The upper limit to the filtration rate is unknown at this time.The test flow sheet is given and preliminary results of a scale-up of 75:1 are presented.
展开▼
机译:本文阐述了从粘性流中分离纳米磁性粒子的潜力,并简要讨论了一种新型的打破乳状液的磁性方法(美国专利5868939),该方法是新型主分离器电磁细颗粒分离器的先驱,(MM-PS,正在申请专利)。本文的其余部分将重点讨论MM-PS,其设计用于在260°C下从费托蜡中高通量等温和等压分离纳米铁催化剂颗粒。固含量为0.3- 0.5 wt%的FT蜡,可在25重量%至2,000高斯的条件下以最高230 kg / min / m〜2的生产速率生产出。目前尚不知道过滤速率的上限。给出了测试流程,并给出了放大比例为75:1的初步结果。
展开▼