The controlled release behavior and pH- and thermo-sensitivity of alginate/poly (vinyl alcohol) blended hydrogels

摘要

Poly(vinyl alcohol) (PVA) was blended with sodium alginate (Alg) in various ratios and crosslinked with calcium chloride and made into hydrogel membranes. The dependence of the swelling behavior of these Alg-Ca/PVA hydrogels on pH was investigated. The temperature-dependent swelling behavior of the semi-interpenetrating network (semi-IPN) hydrogels was examined at temperatures from 2 to 45℃ and the enthalpy of mixing (ΔH{sub}(mix)) was determined at various temperatures. The molecular structure of the hydrogels was studied by infrared spectroscopy and their water structure in the semi-IPN hydrogels was measured by differential scanning calorimetry (DSC). The influence of Ca{sup}(2+) content on the network structure of Alg-Ca/PVA hydrogels was investigated in terms of the compressive elastic modulus, effective crosslinking density, and the polymer-solvent interaction parameter based on the Flory theory. The loading of alizarin red S (ARS) followed the Langmuir isotherm mechanism and the release kinetics of ARS from the Alg-Ca/PVA hydrogels followed the Fickian diffusion mechanism.