Microstructural control of Ni-YSZ cermet anode for planer thin-film solid oxide fuel cells

摘要

Ni-Y_2O_3-stabilized ZrO_2 (Ni-YSZ) cermet anode was fabricated for solid oxide fuel cells (SOFCs) by conventional ceramic processing using NiO-YSZ composite particles. Microstructures of the anode were carefully characterized by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The Ni-YSZ cermet anode was consisting of fine YSZ connections, as the conducting pass of oxygen ions, on the surface of Ni network, as that of electrons, with continuous pore structure and as that of gaseous species. No amorphous phases were present at the interface between Ni and YSZ, and there was an orientation relationship between Ni and YSZ grains, (111)_(Ni)//(111)_(YSZ). The cermet anode showed a high electrical performance at 800℃. These results indicated that the electrochemical activity of the Ni-YSZ cermet anode was enhanced with the present microstructure.