Estimating the Remaining Service Life of Pipeline Bend Metal with Microdamage Based on the Results from Long-Term Strength Tests of Solid and Notched Samples1

V. I. Gladshtein

首页> 外文期刊>Thermal engineering >Estimating the Remaining Service Life of Pipeline Bend Metal with Microdamage Based on the Results from Long-Term Strength Tests of Solid and Notched Samples1

【24h】

Estimating the Remaining Service Life of Pipeline Bend Metal with Microdamage Based on the Results from Long-Term Strength Tests of Solid and Notched Samples1

机译：基于固体和缺口样品的长期强度测试结果估算具有微小损伤的管道弯曲金属的剩余使用寿命1

获取原文

获取原文并翻译 | 示例

获取外文期刊封面封底 >>

开具论文收录证明 >>

文献代查 >>

团队文献服务 >>

页面导航

摘要
著录项
相似文献
相关主题

摘要

The longevity of solid (smooth) and notched samples made of Grade 12KhlMF steel is considered. A combined calculation and experimental dependence for determining the effect of stresses and temperature on the remaining service life of metal damaged by single pores and chains of pores is presented.

机译：考虑了由12KhlMF级钢制成的实心（光滑）和缺口样品的寿命。提出了确定应力和温度对单个孔和孔链损坏的金属的剩余使用寿命的影响的组合计算和实验依赖性。

著录项

来源
《Thermal engineering 》 |2012年第4期| p.295-301| 共7页
作者
V. I. Gladshtein;
展开▼
作者单位

OAO All-Russia Thermal Engineering Institute, Avtozavodskaya ul. 14/23, Moscow, 115280 Russia;

展开▼
收录信息
原文格式 PDF
正文语种 eng
中图分类
关键词

相似文献

外文文献
中文文献
专利

1. Refined Evaluation of the Remaining Service Life of Steam Line Bends by Simulating the Durability of Metal through Tests of Notched Samples [J] . V.I.Gladshtein Thermal engineering . 2011 ,第2期

机译：通过缺口样品测试模拟金属的耐用性，细化评估蒸汽管线弯曲的剩余使用寿命
2. APPLICATION OF THE METHOD OF BASE DIAGRAMS FOR THE PREDICTION OF LONG-TERM STRENGTH IN NOTCHED SPECIMEN TESTS [J] . V. V. Krivenyuk, V. P. Kolyada, M. I. Egorova Strength of Materials . 2003 ,第1期

机译：基图方法在缺口试样测试中的长期强度预测中的应用
3. Diagnostics of Creep in Heat-Resistant Steels II: Calculation of Residual Life of Metal that Functions under Creep Conditions Based on the Results of Testing for Operational Microdamage [J] . V. S. Permikin Russian Journal of Nondestructive Testing . 2011 ,第3期

机译：耐热钢蠕变的诊断II：基于操作性微损伤测试的结果计算在蠕变条件下起作用的金属的剩余寿命
4. Estimating the remaining service life of switchgear insulators: Application of the Mahalanobis-Taguchi (MT) method to diagnosis of degradation and estimation of the remaining service life of insulators [C] . Okazawa Hiroshi, Miki Shinsuke 2012 IEEE International Conference on Condition Monitoring and Diagnosis. . 2012

机译：估计开关设备绝缘子的剩余使用寿命：Mahalanobis-Taguchi（MT）方法在绝缘退化的诊断和估计剩余寿命中的应用
5. Remaining Service Life Estimation and Probabilistic Analysis of Reinforced Concrete Sewer Pipeline Systems [D] . Moamaei, Pardis. 2019

机译：钢筋混凝土污水管道系统的剩余服务寿命估算与概率分析
6. Estimation of Notched Composite Plates Fatigue Life Using Residual Strength Model Calibrated by Step-Wise Tests [O] . Paweł Romanowicz, Aleksander Muc 2018

机译：用逐步检验校准的残余强度模型估算带缺口复合板的疲劳寿命
7. Fatigue Strength under Combined Rotating Bending and Torsional Load : Report 1 Fatigue Life of V-notched S 35 C Steel Specimen under Successive Rotating Bending and Reversed Torsion [O] . Hiroshi NAKAMURA, Saneyasu HOSHI, Itsuro AOKI 1969

机译：组合旋转弯曲和扭转载荷下的疲劳强度：在连续旋转弯曲和逆转扭转下报告V-indched S 35 C钢样品的疲劳寿命
8. Single Edge Notch Specimens of Two High Strength Martensitic Steels Tested in Tension and Bending [R] . Walker, E. F., May, M. J. 1968

机译：两种高强度马氏体钢的单边切口试样张力和弯曲试验

Estimating the Remaining Service Life of Pipeline Bend Metal with Microdamage Based on the Results from Long-Term Strength Tests of Solid and Notched Samples1

摘要

著录项

相似文献

相关主题

期刊订阅