Using room temperature vulcanization process (RTV), based on platinum catalyzed hidrosuylation reaction, two series of siloxane elastomers were obtained in that way, that one poly (dimethul-co-methyulhy-drido)siloxane was cross-linked with different amounts of divinylbenzene- and 1,3 -divinyltetramethyldisiloxane- crosslinking agent. The degrees of crosslinking were experimentally determined via swelling measurements, and they agreed well with the expected values calculated from the intial reaction mixture compositions. The effects of the degree of crosslinking on the hardness and on the storage moduls of elastomers were examined. The results obtained showed that the hardness and the storage moduls both increased with the increase of degree of crosslinking. Also, as expected, the elastomers obtained using a more rigid divinylbenzene crosslinking agent showed higher storage modulus values compared with the corresponding elastomers obtainedwith amore flexible 1,3-divinyltetramethyldisiloxane crosslinking agent.%Vulkanizacijom na sobnoj temperaturi (RTV), baziranoj na reakciji hidrosililovanja između linearnogpo-li-(dimetil-ko-metilhidrido) siloksana i divinibenzena, odnosno 1,3-diviniltetrametildisiloksana, uz plati-nadiviniltetrametildisiloksan kompleks kao katalizator uspešno su sintetizovane dve serije siloksanskih elastomera različitih stepena umreženja. Stepen umreženja je eksperimentalno određen iz stepena bubrenja, i pokazao je dobro slaganje sa očekivanim stepenom umreženja izračunatim iz sastava reakcionih smeša. Ispitan je uticaj stepena umreženja na tvrdoću i modul sačuvane energije (G'') elastomera. Dobijeni rezultati su pokazali da vrednosti za tvrdoću i G'' rastu sa povećanjem stepena umreženja. Takođe, kao što je i bilo očekivano, elastomeri dobijeni sa "krućim" divinilbenzenom kao umreživačem pokazali su veće module G''upoređenju sa odgovarajućim elastomerima koji su dobijeni koristeći "fleksibilniji" 1,3-divinil-tetrametildisiloksan kao umreživač.
展开▼
机译：使用室温硫化工艺（RTV），基于铂催化的水合水合反应，以这种方式获得了两个系列的硅氧烷弹性体，即一种聚（二甲基-共-甲基-干基）硅氧烷与不同量的二乙烯基苯-交联。和1，3-二乙烯基四甲基二硅氧烷交联剂。交联度是通过溶胀测量通过实验确定的，它们与根据初始反应混合物组成计算的预期值非常吻合。检查了交联度对弹性体的硬度和储能模量的影响。所得结果表明，硬度和储能模量均随交联度的增加而增加。同样，正如预期的那样，与使用更高柔性的1,3-二乙烯基四甲基二硅氧烷交联剂获得的相应弹性体相比，使用更高刚性的二乙烯基苯交联剂获得的弹性体显示出更高的储能模量值。线性线性（dimetil-ko-metilhidrido）siloksana i divinibenzena，odnosno 1,3-diviniltetrametildisiloksana，uz plati-nadiviniltetrametildisiloksan kompleks kao katalizatoruspešnosu sintetizovah dve serijeskia Stepenumreženjaje eksperimentalnoodređeniz stepena bubrenja，i pokazao je dobro slaganje saočekivanimstepenomumreženjaizračunatimiz sastava reakcionihsmeša。 Ispitan je uticaj stepenaumreženjanatvrdoćui模制弹性体（G''）弹性体。您可以通过以下方式获得更多资讯：Dobijeni rezultati su pokazali da vrednosti zatvrdoćui G“ rastu sapovećanjemstepenaumreženja。 Takođe，kaoštoje i biloočekivano，弹性体“krućim” divinilbenzenom kaoumreživačempokazali suveće模块G''upoređenjusaodgovarajućim弹性体koji su dobijeni koristeumi” 1到fleksidisni
展开▼