In this study, porous Ni-Ti and Co-Cr-Mo alloy couple was fabricated by powder metallurgy (PM) process. With this aim, Ni-Ti and Co-Cr-Mo alloys powder was compacted into the mould one by one with Co-Cr-Mo being the one side and Ni-Ti the other side. Then, Ni-Ti side of the specimen was synthesised by self-propagating high temperature synthesis (SHS) process. At the end of the SHS process (after the SHS process), the porous Ni-Ti alloy has occurred. Finally, the specimen was sintered at 1050°C into argon atmosphere. Scanning electron microscope with energy dispersive X-ray spectroscopy and X-ray diffractometer were used to characterise the microstructure and composition. It was seen from the results that porous Ni-Ti and Co-Cr-Mo alloy couple was successfully fabricated by PM process.
机译:在这项研究中,通过粉末冶金(PM)工艺制造了多孔Ni-Ti和Co-Cr-Mo合金对。为了这个目的,将Ni-Ti和Co-Cr-Mo合金粉末一个接一个地压制成型,其中Co-Cr-Mo为一侧,Ni-Ti为另一侧。然后,通过自蔓延高温合成(SHS)工艺合成了标本的Ni-Ti面。在SHS工艺结束时(在SHS工艺之后),出现了多孔Ni-Ti合金。最后,将样品在1050℃下烧结到氩气中。用能谱X射线能谱仪和X射线衍射仪对电子显微镜进行了表征。从结果可以看出,通过PM工艺成功地制备了多孔Ni-Ti和Co-Cr-Mo合金对。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱:kefu@zhangqiaokeyan.com

京公网安备:11010802029741号 ICP备案号:京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有
  • 客服微信

  • 服务号