The process of argon-arc welding fuse on a dispersion-hardened composition materials on the basis of Al-Si alloy reinforced with 5 % vol. of SiC particles has been investigated. Two techniques of the fusing process, implying different ways of added material injection, were considered. Metallographic analysis and hardness measurement revealed that when the added material is injected on the front face of the melt bath, uniform distribution of reinforcing particles in weld pad still persists. Results of dry friction tests showed a lower value of friction factor and high wear resistance of the composite material as compared to cast composite materials the same structure.%Исследован процесс аргонодуговой наплавки износостойких покрытий с применением присадочного материала из дисперсно-упрочненного композиционного материала на основе сплава АК12М2МгН, армированного 5 % об. частиц 51С. Рассмотрены две схемы аргонодуговой наплавки, различающиеся способами введения присадочного материала. Методами металлографического анализа и измерения твердости показано, что при введении присадочного материала по переднему фронту ванны в наплавленном слое сохраняется равномерное распределение армирующей фазы. Результаты испытаний на сухое трение скольжения показали, что коэффициент трения наплавленного композиционного материала ниже, а износостойкость выше, чем у литого композиционного материала того же состава.