Наноструктурирование поверхности карбидовольфрам овых твердых сплавов при электровзрывном легировании

摘要

The hardening of hard alloy by influence of impulse plasma jets formed by electric explosion of carbo-gra-phite fiber is conducted. By profilometry, scanning electronic microscopy, X-ray crystal analysis and hardness testing it is established that treatment in low-energy condition without surface melting in exposed to jets surface does not change phase composition of hard alloy. The treatment with surface melting leads to planarization of the surface, forming the zone of influence with higher hardness 20...25 pm in depth. The hardening takes place thanks to the changing of one type of carbide WC in hard alloy to another type W which has higher hardness, and size reduction of Wfi in surface layer.%Проведено упрочнение твердого сплава путем воздействия на поверхность импульсных плазменных струй, сформированных при электрическом взрыве углеграфитовых волокон. Методами профиломет-рии, сканирующей электронной микроскопии, рентгеноструктурного и дюрометрического анализов ус­тановлено, что обработка в низкоэнергетическом режиме без оплавления облучаемой поверхности не меняет фазового состава твердого сплава. Обработка с оплавлением приводит к сглаживанию релье­фа поверхности, образованию зоны воздействия с повышенной твердостью глубиной 20...25 мкм. Уп­рочнение происходит за счет смены типа монокарбида вольфрама WC в твердом сплаве на другой тип WJZ, который обладает большей твердостью, и уменьшения величины карбида вольфрама WjO в по­верхностном слое.