Effect of Natural Antioxidant (Diospyros peregrina) on the Aging Properties of Radiation Vulcanized (γ-Radiation) Natural Rubber Latex Film

摘要

Natural rubber latex and various concentration of natural antioxidant were blended in different ratios and irradiated at various absorbed doses by gamma rays from Co-60 source at room temperature. The aqueous extraction of Diospyros peregrina was used as natural antioxidant. It was found that the addition of different concentration of natural antioxidant into natural rubber latex improve the aging property of the film. Decreasing in tensile strength of rubber film with 10 phr natural antioxidant and 15 kGy radiation dose after 24 hours aging at 100°C was 9.34% compared to 13.89% for film without natural antioxidant. The tensile strength, tear resistance and modulus at 500% elongation of the rubber film were found to be optimum at 15 kGy radiation dose and with 10 phr natural antioxidant. Elongation at break, permanent set and swelling ratio decreases with the increasing absorbed radiation dose as well as the concentration of the natural antioxidant.