親水性骨格を有する高分子液晶のLamgmuir-Blodgett膜形成と光応答

摘要

Liquid crystalline polymers (LCPs) having both hydrophilic and hydrophobic parts are suitable materials for fabrication of oriented thin films by the Langmuir-Blodgett (LB) method. In this research, side-chain LCPs with a polyethyleneimine chain and main chain LCPs with a polyoxyethylene chain were used. All of the LCPs formed a monolayer at the air-water interface. Moreover, their multilayered LB films were obtained on solid substrates. The bulk state of the side chain LCPs showed the multilayered structures with the perpendicular alignment of mesogenic groups similar to the LB films. Main-chain LCPs formed folding structures in the layers of the LB films. In the case of LB films of LCPs with azobenzene pendant groups, the initial periodic structures were rebuilt after the irradiation cycles.%親水性部位を有する側鎖型高分子液晶および主鎖型高分子液晶について気液界面単分子膜ならrnびにLangmuir-Blodgett（LB）膜を作製し，その成膜性，配向構造および光異性化挙動を検討した．親水性rn高分子である分岐状ポリエチレンイミソ（PEI）の側鎖にアゾベンゼソ基を有する側鎖型高分子液晶（IP4，rnNP4）は凝集性の良い単分子膜を形成し，固体基板上に定量的に累積された．ポリオキシエチレン（POE）rn鎖を有する主鋳型高分子液晶（POEBSB-6）は，親水性部位であるPOE鎖の柔軟性によって，高分子鎖が折りたたまれた構造を形成し，メソゲソ基が平行に配列することを見出した．IP4とNP4から作製したrnLB膜では，アゾベンゼソの光異性化によって，ランダム配向と層秩序の状態を可逆的に形成することをrn明らかにした．この可逆的な秩序状態の変化は，高分子液晶がLB膜内においても自己組織化する機能を顕著に示した例である．