Enhanced performance in inverted polymer solar cells via solution process: Morphology controlling of PEDOT:PSS as anode buffer layer by adding surfactants

摘要

Inverted polymer solar cells were fabricated by adding the amphiphilic surfactant 'Surfynol 104 series' to Poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS) as a anode buffer layer by solution process. With the introduction of Surfynol 104 series-added PEDOT:PSS, it was able to form a homogeneous film by adjusting the wettability of a hydro-phobic poly(3-hexylthiophene) (P3HT):[6,6]-phenyl C_(61)-butyric acid methyl ester (PCBM) film. With decrease in series resistance (R_S) and increase in shunt resistance (R_(SH)). as a result, the short circuit current density (J_(SC), open circuit voltage (V_(OC)) and fill factor (FF) of the optimized device were 10.2 mA/cm~2, 0.63 V and 61.3%, respectively, calculated the power conversion efficiency (PCE) was 4.0%. In addition, the air stability of the fabricated device was improved.