Fabrication and laser behaviors of Yb~(3+) doped silica large mode area photonic crystal fiber prepared by sol-gel method

摘要

Yb~(3+), Al~(3+) co-doped silica large mode area photonic crystal fiber (LMA PCF) has been prepared by sol-gel method combined with stack-capillary-draw technique. The core glass with composition of 0.3Yb_2O_3-3Al_2O_3-96.7SiO_2 (mol%) has 927 μs fluorescence lifetime, 0.82 pm~2 stimulated emission cross section at ～1 μm and 1.4 ppm residual hydroxyl group. 6.8 W continuous-wave fiber laser ranging from 1040 to 1070 nm has been obtained from a piece of 98-cm-long PCF with the Yb~(3+) concentration of 6.49 × 10~(19) ions/cm~3 pumped by a commercial 927-nm laser diode. The laser has a threshold of 1.45 W launched power with a slope efficiency of 48%. The maximum output power of 6.8 W is limited by the available pumping power, and the optical loss is 1.2 dB/m at 1053 nm. To the best of our knowledge, this is the highest laser output power report on Yb~(3+), Al~(3+) co-doped silica LMA PCF prepared by sol-gel method.