Kompozyt narzędziowy na osnowie regularnego azotku boru z wieloskładnikową fazą wiążącą

摘要

There are presented the results of tests performed on the tool grade composite metal consisting of isometric boron nitride (cBN) matrix with multiple binder phase built up from titanium compounds obtained by means of high pressure sintering process. The sinters reveal non-porous microstructure and high mechanical properties (Young Module = 550 GPa, Vicker hardness HVm = 29 GPa, fracture toughness 9 MPa ■ m~(1/2)). Hardened steel turning tests have proved the tools made from the tested composite metal demonstrating a dozen times higher durability in comparison with the commercial quality cutting tools. Composites are also noted for good electrical conductivity, which makes it possible to apply the spark erosion methods for their machining.%Przedstawiono wyniki badań kompozytu narzędziowego na osnowie regularnego azotku boru (cBN) z wieloskładnikową fazą wiążącą w postaci związków tytanu, otrzymanego drogą spiekania wysokociśnieniowego. Badane spieki charakteryzują się bez-porowatą mikrostrukturą oraz dobrymi właściwościami mechanicznymi (moduł Younga 550 GPa, twardość HV_(10) 29 GPa, odporność na kruche pękanie 9 MPa m~(1/2)). Technologiczne próby toczenia stali zahartowanej narzędziami wykonanymi z tego kompozytu wykazały ich kilkunastokrotnie większą trwałość w porównaniu z narzędziami komercyjnymi. Kompozyty charakteryzują się również przewodnictwem prądu elektrycznego na poziomie umożliwiającym ich obróbkę metodami elektroerozji.