Badania procesu szlifowania kompozytów BNDCC ściernicami diamentowymi ze spoiwem ceramicznym

摘要

The paper presents effects of grinding the BNDCC composite workpieces by means of recently developed diamond grinding wheels. The wheels used during the tests had the grain size significantly varying: D46 45÷38 μm and D25 30÷20 μm, with the concentration elevated up to C125. The bonding phase was a new formula vitrified bond. Basing on the results of machining process, material removal rate, specific material removal rate and G coefficient were calculated. Also surface quality and topography after machining operation were investigated and parameters reflecting surface roughness profile (2D and 3D) were derived. The relations between process parameters and surface roughness are presented in the form of a second degree polynomial with interactions. The maximum output machining parameters are identified for relevancy with the best surface finish effects.%Przedstawiono wyniki badań procesu szlifowania próbek kompozytowych z BNDCC ściernicami diamentowymi z nowo opracowanymi spoiwami o zróżnicowanej granulacji ziarna diamentowego (D46 45÷38 μm, D25 30÷20 μm) i jego podwyższonej koncentracji (C 125). Obliczono wydajność ubytkową procesu, właściwą wydajność ubytkową i wskaźnik G. Oceniono topografię powierzchni próbek poprzez określenie parametrów profilu chropowatości, obraz 2D i 3D. Zależności pomiędzy parametrami procesu a chropowatością zaprezentowano w postaci wielomianu drugiego stopnia z interakcjami. Określono parametry efektywnej obróbki w połączeniu z najniższą chropowatością.