摘要

Because of their good behavior under irradiation, fuel elements based on U_(3)Si_(2) particles dispersed in an Al matrix have been used to convert to low-enriched uranium in a large number of research reactors. This behavior is extended to any compound grown by interdiffusion between silicide and Al during the fabrication process.In this work, two plates fabricated with U_(3)Si_(2) particles dispersed in an Al matrix were analyzed by optical and scanning electron microscopies, wave length dispersive microanalysis, and X-ray diffraction after the fabrication process. The results show that U(Al,Si)_(3) together with another phase with the same crystalline structure as U_(3)Si_(2) but modified cell volume was formed.A detailed analysis of fuel elements based on U_(3)Si_(2) is considered very useful to be applied when going into greater depth in the frame of a U(Mo) qualification program.